TU00/C10100 oxygen free copper rod

• 

• Material:	TU00/C10100 oxygen free copper rod
  Other Brands:	TU00/C10100 oxygen free copper rod
  Source Stock:	Customized
  Supplier:	Shanghai Hite Special Alloy Co., Ltd.
  Contacts:	Mr.KayDuan
  Email:	sales02@hitealloy.com

• TU00/C10100 oxygen free copper rod Details

  
  
  

  
  

  Brief introduction:

  • Oxygen free copper rod is produced using vacuum horizontal continuous casting and upward drawing method.

  • Extremely low hydrogen and oxygen content.

  • Better ductility and higher conductivity.

  • Small grain size and uniform metallographic structure.

  • High speed cables are not easily broken.

  
  

  Specifications:

  Properties: No hydrogen embrittlement phenomenon, high conductivity, good processing and welding performance, corrosion resistance and low temperature performance.

  Common specifications: Φ 1cm~Φ 8cm (can be customized according to customer requirements, and can selectively remove specified impurities).

  Attribute	Data
  oxygen content	＜3ppm
  Conductivity	58-59MS/m
  Thermal conductivity	394W/(m·K)
  elongation	Soft state：33-40%
  	Semi hard：4-12%
  	Hard state：2-5%
  Hardness HV	Soft state：35-65HV
  	Semi hard：70-110HV
  	Hard state：≥110HV
  tensile strength	Soft state：200-260MPa
  	Semi hard：250-360MPa
  	Hard state：260-400MPa
  yield strength	Soft state：35-140MPa
  	Semi hard：180-280MPa
  	Hard state：220-380MPa
  RRR	≥400
  Metallographic structure	Level 1 or Level 2 metallographic contamination

  
  

  Test report:

  We send our products to testing institutions such as PAT and EAG for quality inspection to ensure the reliability and stability of our products.